Title: Thorium effect on the oxidation of uranium: Photoelectron spectroscopy (XPS/UPS) and cyclic voltammetry (CV) investigation on (U1 − xThx)O2 (x = 0 to 1) thin films
Authors: CAKIR PELINELOIRDI RachelHUBER FrankKONINGS RudyGOUDER Thomas
Citation: APPLIED SURFACE SCIENCE vol. 393 p. 204-211
Publisher: ELSEVIER SCIENCE BV
Publication Year: 2016
JRC N°: JRC102837
ISSN: 0169-4332
URI: http://publications.jrc.ec.europa.eu/repository/handle/JRC102837
DOI: 10.1016/j.apsusc.2016.10.010
Type: Articles in periodicals and books
Abstract: Thin films of U1− xThxO2 (x = 0 to 1) have been deposited via reactive DC sputter technique and characterized by X-ray/Ultra-violet Photoelectron Spectroscopy (XPS/UPS), X-ray Powder Diffractometer (XRD) and Cyclic Voltammetry (CV) in order to understand the effect of Thorium on the oxidation mechanism. During the deposition, the competition between uranium and thorium for oxidation showed that thorium has a much higher affinity for oxygen. Deposition conditions, time and temperature were also the subject of this study, to look at the homogeneity and the stability of the films. While core level and valence band spectra were not altered by the time of deposition, temperature was affecting the oxidation state of uranium and the valence band due to the mobility increase of oxygen through the film. X-ray diffraction patterns, core level spectra obtained for U1 − xThxO2 versus the composition showed that lattice parameters follow the Vegard's law and together with the binding energies of U-4f and Th-4f are in good agreement with literature data obtained on bulk compounds. To study the effect of thorium on the oxidation of U1 − xThxO2 films, we used CV experiments at neutral pH of a NaCl solution in contact with air. The results indicated that thorium has an effect on the uranium oxidation as demonstrated by the decrease of the current of the oxidation peak of uranium. XPS measurements made before and after the CV, showed a relative enrichment of thorium at the extent of uranium at the surface supporting the formation at a longer term of a thorium protective layer at the surface of uranium-thorium mixed oxide.
JRC Directorate:Nuclear Safety and Security

Files in This Item:
There are no files associated with this item.


Items in repository are protected by copyright, with all rights reserved, unless otherwise indicated.