Investigation of Irradiation Hardening and Effectiveness of Post-Irradiation Annealing on the Recovery of Tensile Properties of VVER-1000 RealisticWelds Irradiated in the LYRA-10 Experiment

Assessing the embrittlement and hardening of reactor pressure vessel steels is critical for the extension of the service lifetime of nuclear power plants. This paper summarises the tensile test results on the irradiation behaviour of realistic VVER-1000 welds from the STRUMAT-LTO project. The welds were irradiated at the HFR (Petten, the Netherlands) to a fluence of up to 1.087 × 1020 n·cm−2, and their irradiation hardening was studied by means of tensile testing. The four grades, with different Mn and Ni contents, show different hardening behaviours. The highest degree of irradiation hardening is observed for the weld that has the highest combined Ni + Mn content. The results show that there is a synergetic effect of Mn and Ni on the irradiation hardening behaviour of the VVER-1000 welds. Besides irradiation hardening, the effectiveness of post-irradiation annealing treatments on the recovery of the tensile properties is studied in the present work. Post-irradiation annealing treatments conducted at 418 ◦C and at 475 ◦C proved to be effective for three of the four investigated welds. For the realistic weld with the highest combined Ni + Mn, only the annealing at 475 ◦C led to the complete recovery of the tensile properties.

LAOT Mathilde;  MARQUES PEREIRA Vivian;  BAKKER Theo;  D'AGATA Elio;  MARTIN Oliver;  KOLLURI M.; 

2024-12-16

MDPI

JRC138138

2075-4701 (online),   

https://www.mdpi.com/2075-4701/14/8/887,    https://publications.jrc.ec.europa.eu/repository/handle/JRC138138,   

10.3390/met14080887 (online),