Letter to the Editors. The Effect of Cyclic Loading on the Irradiation Hardening of Type 316L Stainless Steel.
Strain controlled fatigue tests have been performed in torsion on annealed type 316L SS irradiated with 19 MeV deuterons at 400*C for shear strain ranges between .95% and 1.4%. The irradiation hardening of the material was suppressed to a great extent for continuous cycling conditions in comparison to hold time tests.