A STUDY OF PRECIPITATION REACTIONS IN THE CR-MN AUSTENITIC STEEL NITRONIC 32 WAS PERFORMED BY MEANS OF ELECTRON MICROSCOPY, ELECTRON DIFFRACTION, X-RAY MICROANALYSIS AND ELECTRON ENERGY LOSS SPECTROMETRY. THE MATERIAL WAS EXAMINED: A) AFTER SOLUTION ANNEALING AND AGEING AT 773, 1023 AND 1073 K; B) AFTER SOLUTION ANNEALING FOLLOWED BY AMBIENT TEMPERATURE HE-IMPLANTATION AND AGEING AT 773 AND 1923 K AND, C) IN THE SOLUTION ANNEALED STATE FOR COMPARISON. THE FORMATION OF THE PHASES M23C6 AND CR2N WAS OBSERVED. THEIR PRECIPITATION MODES AND SEQUENCE ARE DESCRIBED ABD DISCUSSED.
RUEDL Erich;
1995-03-15
JRC5250
https://publications.jrc.ec.europa.eu/repository/handle/JRC5250,
| Name | Country | City | Type |
|---|
This document is only visible at the Commission level.
You are not authorized to publish or distribute it outside the European Commission.
This is a public document. You can share this publication.
Datasets
| ID | Title | Public URL |
|---|
Dataset collections
| ID | Acronym | Title | Public URL |
|---|
Scripts / source codes
| Description | Public URL |
|---|
Additional supporting files
| File name | Description | File type |
|---|