Mg-8Li alloy reinforced by 7 vol.% SiC particles was processed by a powder metallurgical method. Samples were deformed in tension at temperatures from room temperature up to 300 °C. The yield stress as well as the tensile strength decrease with increasing temperature. Decreasing stresses detected at temperatures higher than 150 °C indicate possible presence of recovery process/es. Estimated activation enthalpy is close to the activation enthalpy for the grain boundary sliding. Strain rate sensitivity was estimated at elevated temperatures. Enhanced plasticity was estimated at 300 °C. Light and scanning electron microscopy revealed the cavitations during the high temperature deformation.
TROJANOVA Zuzanka;
SZARAZ Zoltan;
2012-03-01
Trans Tech Publications
JRC59070
1662-9795,
http://www.scientific.net/KEM.465.378,
https://publications.jrc.ec.europa.eu/repository/handle/JRC59070,
10.4028/www.scientific.net/KEM.465.378,
| Name | Country | City | Type |
|---|
This document is only visible at the Commission level.
You are not authorized to publish or distribute it outside the European Commission.
This is a public document. You can share this publication.
Datasets
| ID | Title | Public URL |
|---|
Dataset collections
| ID | Acronym | Title | Public URL |
|---|
Scripts / source codes
| Description | Public URL |
|---|
Additional supporting files
| File name | Description | File type |
|---|